Semiconductor device including multiple fin heights

ABSTRACT

A semiconductor device comprising a substrate, an base layer disposed on the substrate having a thickness C in first area and a thickness B in a second area and a hole extending to the substrate filled with semiconductor, a first semiconductor fin disposed on the first area and having a height A, and a second semiconductor fin disposed on the second area and having a height D, wherein (A+C)=(B+D).

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a division of U.S. application Ser. No. 14/963,603,filed Dec. 9, 2015, the contents of which are hereby incorporated byreference in its entirety.

BACKGROUND

As semiconductor technology continues to advance and semiconductordevice and structure dimensions continue to decrease a recently evolvingtrend within semiconductor device and structure fabrication has been theadvent of the FinFET device, rather than planar field effect transistordevices. A FinFET device is characterized by a semiconductor fin that ispositioned perpendicularly with respect to a semiconductor substrate, toprovide a vertical channel within the FinFET device. This verticalchannel is covered with a gate dielectric and subsequently with a gateelectrode.

As the complexity of semiconductor devices continue to evolve as well asthe desire for ever smaller devices, new semiconductor devicearchitecture and methods for making semiconductor devices is needed.

SUMMARY

Disclosed herein is a method of making a semiconductor structurecomprising: forming a mask on a first region of a base layer covering asubstrate; removing a portion of the base layer from the unmasked regionsuch that the base layer has at least two thicknesses; removing the maskfrom the base layer having at least two thicknesses; forming at leastone hole in the base layer to reveal the substrate; depositing asacrificial material over the base layer having at least two thicknessesand at least one hole; planarizing the sacrificial material; patterningand etching the sacrificial material to provide an area comprising thehole; disposing a dielectric material over the patterned and etchedsacrificial material; patterning and etching the dielectric material toform trenches extending to the base layer on at least two opposing sidesof the remaining sacrificial material; removing the sacrificial materialbeneath the dielectric material to form a cavity bounded by the trenchesand comprising the hole; forming a semiconductor material in the cavityon the base layer having at least two thicknesses by lateral epitaxialgrowth; removing the dielectric material to expose the semiconductormaterial; patterning and etching the semiconductor material to form afirst fin having a first height and a second fin having a second height,wherein the first height does not equal the second height and the top ofthe first fin and the top of the second fin are equidistant from thesurface of the substrate.

Also disclosed herein is a semiconductor device comprising a substrate,an base layer disposed on the substrate having a thickness C in firstarea and a thickness B in a second area and a hole extending to thesubstrate filled with semiconductor, a first semiconductor fin disposedon the first area and having a height A, and a second semiconductor findisposed on the second area and having a height D, wherein (A+C)=(B+D).

Additional features are realized through the techniques of the presentinvention. Other embodiments are described in detail herein and areconsidered a part of the claimed invention. For a better understandingof the invention with the features, refer to the description and to thedrawings.

BRIEF DESCRIPTION OF THE DRAWINGS

The subject matter which is regarded as the invention is particularlypointed out and distinctly claimed in the claims at the conclusion ofthe specification. The forgoing features are apparent from the followingdetailed description taken in conjunction with the accompanying drawingsin which:

FIG. 1 is a representation of a substrate having a partially masked baselayer.

FIG. 2 is depicts the structure of FIG. 1 after partial removal of theunmasked base layer.

FIG. 3 depicts the structure of FIG. 2 after removal of the partialmask.

FIG. 4 shows the structure of FIG. 3 after the formation of a holethrough the base layer to the substrate.

FIG. 5 shows the deposition of sacrificial material on the structure ofFIG. 4.

FIG. 6 depicts the structure of FIG. 5 after planarization.

FIG. 7A is a top view after patterning and etching the sacrificialmaterial.

FIG. 7B is a cross section after patterning and etching the sacrificialmaterial.

FIG. 8 shows the structure of FIG. 7B after a dielectric material hasbeen deposited.

FIG. 9A is a top view after trenches have been etched in the structureof FIG. 8.

FIG. 9B is a cross section showing the location of the trenches.

FIG. 10 shows the structure of FIG. 9B after removal of the sacrificialmaterial.

FIG. 11 shows the structure of FIG. 10 after epitaxial growth of asemiconductor.

FIG. 12 shows the fins formed by removing the dielectric and patterningand removing the semiconductor.

FIG. 13 shows a completed semiconductor device.

DETAILED DESCRIPTION

Described herein is a method of making a semiconductor structure havingfins of differing channels heights while the overall vertical height isthe same. Having differing channel heights increases the options foroverall design and allows form more diverse devices on a singlesubstrate. Having the same overall vertical height simplifiesmanufacturing and makes the manufacturing process more reliable androbust. For example, subsequent gate formation frequently involvesplanarization steps. When the tops of the fins are coplanar itsimplifies any planarization processes. The method comprises removing aportion of the base layer and forming the material for the fin on thebase layer having differing heights in a way so as to form vertical finshaving the same overall height but differing channel heights.

The following definitions and abbreviations are to be used for theinterpretation of the claims and the specification. As used herein, theterms “comprises,” “comprising,” “includes,” “including,” “has,”“having,” “contains” or “containing,” or any other variation thereof,are intended to cover a non-exclusive inclusion. For example, acomposition, a mixture, process, method, article, or apparatus thatcomprises a list of elements is not necessarily limited to only thoseelements but can include other elements not expressly listed or inherentto such composition, mixture, process, method, article, or apparatus.

As used herein, the terms “invention” or “present invention” arenon-limiting terms and not intended to refer to any single aspect of theparticular invention but encompass all possible aspects as described inthe specification and the claims.

With reference now to FIG. 1, a mask 10 is disposed on a base layer 20.Exemplary mask materials include, for example, silicon oxide, siliconnitride (SiN), silicon oxide carbonitride (SiOCN), silicon borocarbonitride (SiBCN), and combinations comprising one or more of theforegoing. The base layer 20 is disposed on a substrate 30. The baselayer comprises a dielectric material. Exemplary dielectric materialscomprise oxides, nitrides, oxynitrides, silicates (e.g., metalsilicates), aluminates, titanates, nitrides, or any combination thereof.The base layer has a starting thickness of 50 to 500 nanometers, or,more specifically, 100 to 250 nanometers.

The substrate comprises a semiconductor material such as silicon,silicon-germanium, III-V materials, or a combination of two or more ofthe foregoing. As used herein, the term “III-V semiconductor” denotes asemiconductor material that includes at least one element from Group IIIof the Periodic Table of Elements (B, Al, Ga, In) and at least oneelement from Group V of the Periodic Table of Elements (N, P, As, Sb,Bi). Typically, the III-V semiconductors may be binary alloys, ternaryalloys, or quaternary alloys, of III-V elements. Examples of III-Vsemiconductors that can be used in the present invention include, butare not limited to GaAs, InAs, InP, InGaAs, InAlAs, InAlAsSb, InAlAsP,AlInGaP, InGaAsP, and alloys thereof.

A portion of the unmasked base layer is removed as shown in FIG. 2. Insome embodiments 5 to 90% of the original base layer thickness isremoved. The minimum thickness for the base layer after removal is 10 to20 nanometers. The base layer can be removed by etching. Exemplary etchprocesses include dry etching processes and wet etching processes. Dryetching includes, for example, reactive ion etching (RIE), ion beametching, or plasma etching. The dry etching process may be combined witha wet etching process. Following removal of a portion of the base layer,the mask 10 is removed and results in the structure shown in FIG. 3.FIG. 3 shows the substrate 30 and the base layer 20 where the base layerhas at least two regions with differing thicknesses. It is explicitlycontemplated that the base layer can comprise three or more thicknessesby repeating the mask and removal steps.

After the mask and base layer removal steps are complete, a holeextending from the surface of the base layer to the substrate is formedusing patterning and etching. Patterning is the shaping or altering ofdeposited materials, and is generally referred to as lithography. Forexample, in conventional lithography, the material is coated with achemical called a photoresist; then, a machine called a stepper focuses,aligns, and moves a mask, exposing select portions of the material belowto short wavelength light; the exposed regions are washed away by adeveloper solution. After etching or other processing, the remainingphotoresist is removed. Exemplary patterning methods include opticallithography, electron-beam lithography, and nanoimprint lithography.FIG. 4 shows the hole 25. A sacrificial material, 40, is then depositedin the hole and over the base layer as shown in FIG. 5. Exemplarysacrificial materials include silicon nitride, aluminum oxide, hafniumoxide, titanium nitride or amorphous silicon. The sacrificial layer canbe deposited using any appropriate method including thermal oxidation,physical vapor deposition (PVD), plasma enhanced chemical vapordeposition (PECVD), microwave enhanced chemical vapor deposition(MECVD), chemical vapor deposition (CVD), electrochemical deposition(ECD), molecular beam epitaxy (MBE) and more recently, atomic layerdeposition (ALD), e-beam evaporation, and sputtering, among others.

The sacrificial material is planarized as shown in FIG. 6. Thesacrificial material can be planarized using chemical mechanicalplanarization. After planarization the sacrificial material may have aheight of 20 to 200 nanometers above the top of the highest point of thebase layer. The sacrificial material is patterned and etched to defineactive areas where later fins will be formed. The area for formation offins includes the hole in the oxide which is filled with the sacrificialmaterial. A top view is shown in FIG. 7A. FIG. 7A shows sacrificialmaterial 40 disposed on a portion of base layer 20. FIG. 7B is a crosssection of FIG. 7A along line A-A. FIG. 7B shows sacrificial layer 40disposed on a portion of base layer 20 and in hole 25.

After the sacrificial material is patterned and etched a dielectricmaterial 50 is deposited over the sacrificial material as shown in FIG.8. Exemplary dielectric materials include silicon oxide, silicon nitride(SiN), silicon oxide carbonitride (SiOCN), silicon boro carbo nitride(SiBCN), spin-on glass, flowable oxide, high density plasma oxide,borophosphosilicate glass, oxides, nitrides, and oxynitrides. Thedielectric material should have a sufficient etch selectivity relativeto base layer 20. In some embodiments base layer 20 is silicon oxide,dielectric material 50 is silicon boro carbo nitride (SiBCN) andsacrificial material 40 is silicon nitride. The dielectric material 50is patterned and etched to form trenches extending to the base layer onat least two opposing sides of the remaining sacrificial material asshown in FIGS. 9A and 9B. The sacrificial material is then removed by asuitable etching process, such as, for example wet etching to form acavity 70 bounded by the trenches and including the hole as shown inFIG. 10. Semiconductor material 80 is then formed in the cavity byepitaxial lateral overgrowth as shown in FIG. 11. Methods for theepitaxial lateral overgrowth include metal organic chemical vapordeposition (MOCVD), metal organic vapor phase epitaxy (MOVPE), plasmaenhanced chemical vapor deposition (PECVD), remote plasma enhancedchemical vapor deposition (RP-CVD), molecular beam epitaxy (MBE),hydride vapor phase epitaxy (HVPE), or liquid phase epitaxy (LPE). Byforming the semiconductor material in a bounded cavity the semiconductormaterial has at least two thicknesses but the upper surface of thesemiconductor material is substantially equidistant from the surface ofthe substrate. Exemplary semiconductors include silicon,silicon-germanium, III-V materials, or a combination of two or more ofthe foregoing. The semiconductor of the substrate 30 and semiconductor80 may be the same or different. In some embodiments the semiconductor80 comprises a III-V material, more specifically, InGaAs, InGaSb orGaAs.

The dielectric material 50 is then removed by etching to expose thesemiconductor material. Exemplary etch processes include dry etchingprocesses and wet etching processes. Dry etching includes, for example,reactive ion etching (RIE), ion beam etching, and plasma etching. Thedry etching process may be combined with a wet etching process. Thesemiconductor material is then patterned and etched to form a first fin90 and a second fin 100. As shown in FIG. 12, fin 90 having a height Ais disposed on oxide having a thickness C and fin 100 having a height Dis disposed on oxide having a thickness B. The sum of A and C is equalto the sum of D and C. Fin 90 and fin 100 can have the same or differentwidths. In some embodiments fin 90 and fin 100 have a width of 4 to 12nanometers. Within this range the width can be 6 to 8 nanometers. Thespacing between the fins is a result of the patterning and the spacingbetween the fins can be the same or different.

Following the completion of the semiconductor structure shown in FIG.12, additional conventional processing techniques are performed (e.g.,gate oxide formation on the fin sidewalls, gate conductor deposition andpatterning, source/drain extension formation, halo formation, spacerformation, source/drain region formation, deposition and planarizationof a blanket dielectric later, contact formation, etc.) so as tocomplete the semiconductor device.

Accordingly, a semiconductor device comprises a substrate, a base layerdisposed on the substrate having a thickness C in first area and athickness B in a second area and a hole extending to the substratefilled with semiconductor, a first semiconductor fin disposed on thefirst area and having a height A, and a second semiconductor findisposed on the second area and having a height D, wherein (A+C)=(B+D).The disclosed semiconductor structure allows different multi-gatenon-planar field effect transistors to be formed on the same substrate.Furthermore, it allow for the first and second semiconductors to beformed from a single semiconductor conductor. It is contemplated thatthe first and second semiconductor fins can be each be made of a singlesemiconductor but each be made of a different single semiconductor. Forexample, the first semiconductor fin can be made of silicon germaniumwhile the second semiconductor fin can be made of silicon. When thefirst and second fins are made of different single semiconductors it isanticipated that the process will require an additional hole extendingto the substrate to function as a seed region for the epitaxial growthof the second semiconductor. It is also expressly contemplated that thefirst and second fins can comprise the same single semiconductormaterial, for example, silicon.

In some embodiments the first fin and the second fin have a width of 4to 12 nanometers. Within this range the width can be 6 to 8 nanometers.The first fin and the second fin can have the same width or they canhave different widths.

In some embodiments, the a semiconductor device comprises a substrate, abase layer disposed on the substrate having a thickness C in first areaand a thickness B in a second area and a hole extending to the substratewherein the hole is filled with semiconductor, a first semiconductor findisposed on the first area and having a height A, and a secondsemiconductor fin disposed on the second area and having a height D,wherein (A+C)=(B+D). The substrate comprises silicon. The base layercomprises silicon oxide. The first semiconductor fin comprises a III-Vsemiconductor such as InGaAs. The second semiconductor fin comprisesIII-V semiconductor such as InGaAs. The thickness B is 5 to 90% ofthickness C.

A completed semiconductor device is shown in FIG. 13. FIG. 13 is atransverse view along fin 100. Similar structure would be seen in atransverse view along fin 90. Source and drain regions 120 flank thereplacement metal gate stacks 110 over the channel regions of the fin100. The replacement metal gate stacks 110 are capped with a cappinglayer.

The gate stacks 110 include high-k metal gates formed, for example, byfilling a dummy gate opening (not shown) with one or more high-kdielectric materials, one or more workfunction metals, and one or moremetal gate conductor materials. The high-k dielectric material(s) can bea dielectric material having a dielectric constant greater than 4.0,7.0, or 10.0. Non-limiting examples of suitable materials for the high-kdielectric material include oxides, nitrides, oxynitrides, silicates(e.g., metal silicates), aluminates, titanates, nitrides, or anycombination thereof. Examples of high-k materials include, but are notlimited to, metal oxides such as hafnium oxide, hafnium silicon oxide,hafnium silicon oxynitride, lanthanum oxide, lanthanum aluminum oxide,zirconium oxide, zirconium silicon oxide, zirconium silicon oxynitride,tantalum oxide, titanium oxide, barium strontium titanium oxide, bariumtitanium oxide, strontium titanium oxide, yttrium oxide, aluminum oxide,lead scandium tantalum oxide, and lead zinc niobate. The high-k materialmay further include dopants such as, for example, lanthanum andaluminum.

The high-k dielectric material layer may be formed by suitabledeposition processes, for example, chemical vapor deposition (CVD),plasma-enhanced chemical vapor deposition (PECVD), atomic layerdeposition (ALD), evaporation, physical vapor deposition (PVD), chemicalsolution deposition, or other like processes. The thickness of thehigh-k dielectric material may vary depending on the deposition processas well as the composition and number of high-k dielectric materialsused. The high-k dielectric material layer may have a thickness in arange from about 0.5 to about 20 nm.

The work function metal(s) may be disposed over the high-k dielectricmaterial. The type of work function metal(s) depends on the type oftransistor and transistor material and may differ between the NFET andthe PFET. Non-limiting examples of suitable work function metals forsilicon or silicon germanium include p-type work function metalmaterials and n-type work function metal materials. P-type work functionmaterials include compositions such as ruthenium, palladium, platinum,cobalt, nickel, and conductive metal oxides, or any combination thereof.N-type metal materials include compositions such as hafnium, zirconium,titanium, tantalum, aluminum, metal carbides (e.g., hafnium carbide,zirconium carbide, titanium carbide, and aluminum carbide), aluminides,or any combination thereof.

A conductive metal is deposited over the high-k dielectric material(s)and workfunction layer(s) to form the gate stacks. Non-limiting examplesof suitable conductive metals include aluminum (Al), platinum (Pt), gold(Au), tungsten (W), titanium (Ti), or any combination thereof. Theconductive metal may be deposited by a suitable deposition process, forexample, CVD, PECVD, PVD, plating, thermal or e-beam evaporation, andsputtering.

A planarization process, for example, chemical mechanical planarization(CMP), is performed to polish the surface of the conductive gate metal.

The descriptions of the various embodiments of the present inventionhave been presented for purposes of illustration, but are not intendedto be exhaustive or limited to the embodiments disclosed. Manymodifications and variations will be apparent to those of ordinary skillin the art without departing from the scope and spirit of the describedembodiments. The terminology used herein was chosen to best explain theprinciples of the embodiments, the practical application or technicalimprovement over technologies found in the marketplace, or to enableothers of ordinary skill in the art to understand the embodimentsdisclosed herein.

The corresponding structures, materials, acts, and equivalents of allmeans or step plus function elements in the claims below are intended toinclude any structure, material, or act for performing the function incombination with other claimed elements as specifically claimed. Thedescription of the present invention has been presented for purposes ofillustration and description, but is not intended to be exhaustive orlimited to the invention in the form disclosed. Many modifications andvariations will be apparent to those of ordinary skill in the artwithout departing from the scope and spirit of the invention. Theembodiment was chosen and described in order to best explain theprinciples of the inventive teachings and the practical application, andto enable others of ordinary skill in the art to understand theinvention for various embodiments with various modifications as aresuited to the particular use contemplated.

The diagrams depicted herein are just one example. There may be manyvariations to this diagram or the operations described therein withoutdeparting from the spirit of the invention. For instance, the operationsmay be performed in a differing order or operations may be added,deleted or modified. All of these variations are considered a part ofthe claimed invention.

While various embodiments have been described, it will be understoodthat those skilled in the art, both now and in the future, may makevarious modifications which fall within the scope of the claims whichfollow. These claims should be construed to maintain the properprotection for the invention first described.

What is claimed is:
 1. A semiconductor device comprising: a substrate; abase layer disposed on the substrate having a thickness C in first areaand a thickness B in a second area and a hole extending to the substratefilled with semiconductor, the base layer including an upper surface; afirst semiconductor fin disposed on the first area and having a heightA, the first semiconductor fin being in contact with the upper surfaceof the first area of the base layer; and a second semiconductor findisposed on the second area and having a height D, the secondsemiconductor fin being in contact with the upper surface of the secondarea of the base layer, wherein (A+C)=(B+D).
 2. The semiconductor deviceof claim 1 wherein the first semiconductor fin comprises a singlesemiconductor material.
 3. The semiconductor device of claim 1 whereinthe second semiconductor fin comprises a single semiconductor material.4. The semiconductor device of claim 1, wherein the first and secondsemiconductor fin comprise a single semiconductor material.
 5. Thesemiconductor device of claim 1, wherein the first and secondsemiconductor fin comprise the same semiconductor material.
 6. Thesemiconductor device of claim 1, wherein the first semiconductor fincomprises silicon, silicon-germanium, a III-V material, or a combinationof two or more of the foregoing.
 7. The semiconductor device of claim 1,wherein the second semiconductor fin comprises silicon,silicon-germanium, a III-V material, or a combination of two or more ofthe foregoing.